Highly Porous Open Cell Nickel Metallic Foam Sheet
Introducción
- This product usesnickel metal foamas the carrier, with stable performance, large specific surface area and high catalytic efficiency, and is widely used in air conditioners, air purifiers, hospitals and other fields.
2. Compared with traditional aluminum based honeycomb networks, the effective contact area has been greatly increased, and the ability to receive ultraviolet light has also been greatly improved. The coarse pore sponge filter is made by processing ordinary open cell soft foam through mesh processing. The mesh processing removes the original facial mask or wall film between foam networks, and obtains the main skeleton mesh structure. The porosity of the foam plastic is up to 97%, which has excellent air permeability, good flexibility and high mechanical strength.
3. Foam nickel production uses mesh foam as filter material, which has the advantages of low flow resistance and high filtration rate. Can effectively filter out particles with a diameter of 15UM. Mesh bubbles have many special uses, such as being used as filtering materials, fuel tank filling materials, and fabric processing materials.
Especificaciones
| Tipo | Célula abierta |
| Pureza | > 99,991 TP3T |
| Formulario | Lámina o rollo, dependiendo del tamaño y el grosor. |
| Tamaño de celda (PPI) | 5-1300 ppp, según solicitud. |
| Espesor | Estándar: 0,08-30 mm |
| Tamaño y forma | Estándar: 500*500 mm/200*300 mm; se puede fabricar en diferentes formas según se solicite. |
| Porosidad | 95%-98% |
| Tasa de celda abierta | ≥98 % |
| Densidad volumétrica | >0,1 g/cm3, según solicitud. |
| Densidad superficial | 200-3500 g/m 2, según lo solicitado
Estándar: 320 ± 20 g/m2 |
| Conductividad térmica (teórica) | >3 W/M.K |
| Resistencia mecánica (teórica) | ≥2~7 MPa |
| Resistencia media a la tracción (N/20 mm) | Vertical ≥ 30, horizontal ≥ 25 |
| Resistencia a la temperatura (teórica) | ≥500 ℃, según solicitud |
| Apariencia | Gris plateado, sin defectos tales como manchas negras, agujeros ciegos, agujeros pasantes, grietas, etc. |
| Composición química | Ni: ≥99,51 % Fe ≤0,0201 % C ≤0,0301 % P ≤0,0101 % S ≤0,0081 % Si ≤0,0051 % Cu ≤0,0101 % |
| Eficacia del blindaje | 200 kHz |
| 40 dB~50 dB | |
| Flexibilidad | Vertical ≥ 5, horizontal ≥ 15 |
| Índice de elongación (%) | Vertical ≥ 5, horizontal ≥ 10 |
| Resistividad eléctrica (m Ω/100 * 10 m)2) | Vertical ≤ 65, horizontal ≤85 |
Dimensión (Espesor* Longitud*Anchura)
| 0,08 mm*300 mm*200 mm | 0,2 mm × 200 mm × 300 mm | 0,3 mm × 200 mm × 300 mm |
| 0,5 mm × 200 mm × 300 mm | 0,7 mm × 200 mm × 300 mm | 0,9 mm*200 mm*300 mm |
| 1,0 mm × 200 mm × 300 mm | 1,3 mm*200 mm*300 mm | 1,5 mm × 200 mm × 300 mm |
| 1,7 mm*200 mm*300 mm | 2,0 mm × 200 mm × 300 mm | 5 mm × 200 mm × 300 mm |
| 10mm*200mm*300mm | 30mm*200mm*300mm | El tamaño se puede personalizar. |